AUSTENITICOS |
FERRITICO |
| # AISI |
303 |
304 |
304L |
316 |
316L |
430 |
| COMPOSICIÓN
QUÍMICA TÍPICA (% en peso) |
| Carbono |
0.15 max. |
0.08 max. |
0.03 max. |
0.08 max. |
0.03 max |
0.12 max. |
| Cromo |
17.0-19.0 |
18.0-20.0 |
18.0-20.0 |
16.0-18.0 |
16.0-18.0 |
14.0-18.0 |
| Niquel |
8.0-10.0 |
8.0-11.0 |
8.0-12.0 |
10.0-14.0 |
12.0-16.0 |
|
| Manganeso |
2 max. |
2 max. |
2 max. |
2 max. |
2.0-3.0 |
1 max. |
| Silicio |
1 max. |
1 max. |
0.75max |
1 max. |
1 max. |
1 max. |
| Fósforo |
0.20 max. |
0.04max. |
0.04 max |
0.04 max |
0.04 max. |
0.04 max |
| Azufre |
0.15 min. |
0.03 max. |
0.03 max |
0.03 max. |
0.03 max. |
0.03 max. |
|
Otros elementos |
Mo. 0.6 max |
|
|
Mo. 2-3 |
Mo. 2-3 |
|
| Se 0.07
min. |
|
|
|
|
|
| PROPIEDADES
FÍSICAS |
| Densidad:
g/cm2 |
8.027 |
8.027 |
8.027 |
8.027 |
8.027 |
7.75 |
| Punto de
fusión: °C |
1400-1420 |
1400-1450 |
1400-1450 |
1370-1400 |
1370-1400 |
1430-1510 |
| Estructura |
Austenítico |
Austenítico |
Austenítico |
Austenítico |
Austenítico |
Ferrítico |
| CALOR
ESPECIFICO Calorías / g °C (0/100°C) |
0.12 |
0.12 |
0.12 |
0.12 |
0.12 |
0.11 |
|
CONDUCTIVIDAD TÉRMICA |
|
Calorías / cm seg.
°C(a 20°C) |
0.035 |
0.035 |
0.035 |
0.035 |
0.035 |
0.06 |
| COEFICIENTE DE
LA EXPANSIÓN |
|
10-6mm °C
(20°C a 100°C) |
16.5 |
16.5 |
16.5 |
15.2 |
15.2 |
10 |
| (20°C a
500°C) |
18.5 |
18.5 |
18.5 |
19.0 a 800° |
19.0 a 800° |
11.2 |
| RESIST.
ELÉCTRICA ESPECIFICA A TEMP. BAJO TECHO |
| Microhomios-cm
a 20°C |
72 |
72 |
72 |
74 |
74 |
60 |
| PERMEABILIDAD
MAGNÉTICA |
| A 200 H. |
1.02 |
1.02 |
1.02 |
1.02 |
1.02 |
Magnético |
| PROPS. MECÁNICAS
A TEMPERATURAS BAJO TECHO |
|
Alargamiento en 50.8mm% |
60 |
60 |
60 |
55 |
55 |
30 |
| Reducción
de área% |
60 |
70 |
70 |
70 |
70 |
55 |
| Carga de
rotura kg/mm2 |
70.3 |
59.7 |
59.7 |
59.7 |
57.0 |
52.7 |
| Dureza
Brinel |
160 |
150 |
145 |
165 |
150 |
155 |
| Dureza
Rockwell B |
80 |
80 |
77 |
85 |
80 |
80 |